Understanding structure–property relationships of main chain cyclopropane in linear polyesters

Connor Stubbs, Andrew Dove

Research output: Contribution to journalArticlepeer-review

278 Downloads (Pure)

Abstract

Rigid ring structures have gained increasing interest in the polymer materials community as an effective means to manipulate bulk properties. Despite this, little work has focussed on the smallest ring: cyclopropane. Herein, we report a polymerisation that enables incorporation of stereopure cis and trans 1,2-cyclopropanedimethanol through the thiol-Michael “click” reaction between dithiol and diacrylate monomers. Polyesters containing a cyclopropane backbone were found to be amorphous, whilst comparable polymers with a 1,4-butanediol backbone were semi-crystalline. By copolymerising cyclopropane monomers at varying ratios with 1,4-butanediol monomers, the crystalinity of the resulting polymer could be effectively tuned. Successfully adjusting the resulting crystallinity resulted in control over the ultimate tensile strength (UTS) and the Young's modulus (E) of the material. Generally, it was found that increasing cyclopropane content led to a decreased UTS and E as a result of lower polymer crystalinity. Effects of cyclopropane stereochemistry on thermomechanical properties were found to be minimal at low cyclopropane backbone ratios.
Original languageEnglish
Pages (from-to)6251-6258
Number of pages8
JournalPolymer Chemistry
Volume11
Issue number39
Early online date28 Aug 2020
DOIs
Publication statusPublished - 21 Oct 2020

Keywords

  • cyclopropane rings
  • stereochemistry

Fingerprint

Dive into the research topics of 'Understanding structure–property relationships of main chain cyclopropane in linear polyesters'. Together they form a unique fingerprint.

Cite this