Abstract
Hydrothermal synthesis in conjunction with colloidal processing has been used to make PZT films in an aqueous solution. Fine PZT powders with a particle size of 200 nm and a narrow particle size distribution were synthesised hydrothermally at 300 degreesC. After washing, a dispersant (di-ammonium citrate) was added to the slurry to make a stable suspension. Electrophoretic deposition (EPD) was then employed to deposit PZT films directly from the hydrothermal PZT suspensions. The effects of the synthesis conditions on the particle size and size distribution of the PZT powders are briefly discussed. Various stabilisation mechanisms for the hydrothermal slurries have been investigated. The effects of the slurry properties and deposition parameters on the microstructure of deposited films are discussed. It is shown that PZT films with a thickness <5 m can be deposited via EPD on Pt wires. However, the limitation of electric field, which must be below the decomposition voltage of water, resulted in an inferior packing density during deposition. The films had to be sintered at relatively higher sintering temperatures (> 1000 degreesC) in comparison with powder compacts. In addition, interaction with the substrate was observed when PZT films were deposited and sintered on Pt-coated alumina substrates. (C) 2001 Elsevier Science Ltd. All rights reserved.
Original language | English |
---|---|
Pages (from-to) | 1539-1542 |
Number of pages | 4 |
Journal | Journal of the European Ceramic Society |
Volume | 21 |
Issue number | 10-11 |
DOIs | |
Publication status | Published - 1 Jan 2001 |
Keywords
- suspensions
- hydrothermal
- films
- PZT