Compositions of Gamma and Gamma Prime Phases in an As-Cast Nickel-Based Single Crystal Superalloy Turbine Blade

The core and the interdendritic regions of an as-cast nickel based single crystal turbine blade were observed by electron microscopy to understand the microstructural development during an investment casting process. The dendrite core region shows an irregular morphology of gamma prime in gamma due to a relatively short casting time, which prevented the development of gamma prime expected in a solution heat-treated microstructure. By comparison, the interdendritic region comprises three different regions composed of: several elongated gamma prime particles, relatively tiny and irregular gamma prime, and gamma prime with relatively regular morphology. The chemical analysis of these phases showed that, regardless of the analysis point in the core or the interdendritic region, almost the same compositions were acquired in the regular type of gamma and gamma prime phases. This result suggests that if the gamma prime forms in the gamma matrix, the composition of gamma prime is almost uniform regardless of the region and prevailing general chemical composition. In contrast, the composition of the elongated gamma prime in the interdendritic region was slightly different depending on the analysis point even within the same elongated particle.