Tribological performance of surface engineered low-cost beta titanium alloy

Research output: Contribution to journalArticlepeer-review

Standard

Tribological performance of surface engineered low-cost beta titanium alloy. / Redmore, Eleanor; Li, Xiaoying; Dong, Hanshan.

In: Wear, Vol. 426-427, No. Part B, 30.04.2019, p. 952-960.

Research output: Contribution to journalArticlepeer-review

Harvard

APA

Vancouver

Author

Bibtex

@article{92ecd310503e4ee48ab0d34197ee8efb,
title = "Tribological performance of surface engineered low-cost beta titanium alloy",
abstract = "Low-cost beta (LCB) alloy (Ti-6.8Mo-4.5Fe-1.5Al) is developed specifically for non-aerospace (e.g. automotive and motor sports) applications. However, as for all other titanium alloys, LCB alloy is characterised by a high and unstable coefficient of friction and a strong scuffing tendency. Hence, a new surface engineering process based on optimal integration of bulk heat treatment with surface ceramic conversion has been developed, and this paper reports the tribological performance of surface engineered LBC titanium alloy. TEM analysis carried out on the microstructure of the ceramic conversion layer. Reciprocating pin-on-disc sliding wear tests were conducted against both WC and hardened steel balls under unlubricated and oil lubricated conditions. Post-examination of the wear tracks, counterparts and wear debris was carried out to investigate the wear mechanisms involved.The experimental results show that the wear resistance of the LCB alloy can be improved by 4-16 times by the novel combined bulk/surface treatment; the coefficient of friction is reduced from 0.8-1.0 for the untreated material to 0.2-0.4 for the treated samples. The wear mechanisms evolve from severe adhesive wear for the untreated material to mild abrasive wear for the treated material when sliding against a WC-Co ball in air. However, severe wear to the steel counterpart occurred and hence large frictional forces formed, which led to delamination wear of treated surfaces. It is also interesting to find that oil lubrication cannot reduce but rather increases the wear of treated surfaces especially when sliding against a hardened steel ball mainly due to oil pressure induced delamination wear.",
keywords = "Ceramic conversion, Combined bulk and surface treatment, Low-cost beta alloy, Reciprocating sliding wear, Solution & ageing",
author = "Eleanor Redmore and Xiaoying Li and Hanshan Dong",
year = "2019",
month = apr,
day = "30",
doi = "10.1016/j.wear.2019.01.032",
language = "English",
volume = "426-427",
pages = "952--960",
journal = "Wear",
issn = "0043-1648",
publisher = "Elsevier",
number = "Part B",

}

RIS

TY - JOUR

T1 - Tribological performance of surface engineered low-cost beta titanium alloy

AU - Redmore, Eleanor

AU - Li, Xiaoying

AU - Dong, Hanshan

PY - 2019/4/30

Y1 - 2019/4/30

N2 - Low-cost beta (LCB) alloy (Ti-6.8Mo-4.5Fe-1.5Al) is developed specifically for non-aerospace (e.g. automotive and motor sports) applications. However, as for all other titanium alloys, LCB alloy is characterised by a high and unstable coefficient of friction and a strong scuffing tendency. Hence, a new surface engineering process based on optimal integration of bulk heat treatment with surface ceramic conversion has been developed, and this paper reports the tribological performance of surface engineered LBC titanium alloy. TEM analysis carried out on the microstructure of the ceramic conversion layer. Reciprocating pin-on-disc sliding wear tests were conducted against both WC and hardened steel balls under unlubricated and oil lubricated conditions. Post-examination of the wear tracks, counterparts and wear debris was carried out to investigate the wear mechanisms involved.The experimental results show that the wear resistance of the LCB alloy can be improved by 4-16 times by the novel combined bulk/surface treatment; the coefficient of friction is reduced from 0.8-1.0 for the untreated material to 0.2-0.4 for the treated samples. The wear mechanisms evolve from severe adhesive wear for the untreated material to mild abrasive wear for the treated material when sliding against a WC-Co ball in air. However, severe wear to the steel counterpart occurred and hence large frictional forces formed, which led to delamination wear of treated surfaces. It is also interesting to find that oil lubrication cannot reduce but rather increases the wear of treated surfaces especially when sliding against a hardened steel ball mainly due to oil pressure induced delamination wear.

AB - Low-cost beta (LCB) alloy (Ti-6.8Mo-4.5Fe-1.5Al) is developed specifically for non-aerospace (e.g. automotive and motor sports) applications. However, as for all other titanium alloys, LCB alloy is characterised by a high and unstable coefficient of friction and a strong scuffing tendency. Hence, a new surface engineering process based on optimal integration of bulk heat treatment with surface ceramic conversion has been developed, and this paper reports the tribological performance of surface engineered LBC titanium alloy. TEM analysis carried out on the microstructure of the ceramic conversion layer. Reciprocating pin-on-disc sliding wear tests were conducted against both WC and hardened steel balls under unlubricated and oil lubricated conditions. Post-examination of the wear tracks, counterparts and wear debris was carried out to investigate the wear mechanisms involved.The experimental results show that the wear resistance of the LCB alloy can be improved by 4-16 times by the novel combined bulk/surface treatment; the coefficient of friction is reduced from 0.8-1.0 for the untreated material to 0.2-0.4 for the treated samples. The wear mechanisms evolve from severe adhesive wear for the untreated material to mild abrasive wear for the treated material when sliding against a WC-Co ball in air. However, severe wear to the steel counterpart occurred and hence large frictional forces formed, which led to delamination wear of treated surfaces. It is also interesting to find that oil lubrication cannot reduce but rather increases the wear of treated surfaces especially when sliding against a hardened steel ball mainly due to oil pressure induced delamination wear.

KW - Ceramic conversion

KW - Combined bulk and surface treatment

KW - Low-cost beta alloy

KW - Reciprocating sliding wear

KW - Solution & ageing

UR - http://www.scopus.com/inward/record.url?scp=85059853539&partnerID=8YFLogxK

U2 - 10.1016/j.wear.2019.01.032

DO - 10.1016/j.wear.2019.01.032

M3 - Article

VL - 426-427

SP - 952

EP - 960

JO - Wear

JF - Wear

SN - 0043-1648

IS - Part B

ER -