The effect of the heat treatments on the tool wear of hybrid Additive Manufacturing of IN718

Research output: Contribution to journalArticlepeer-review

Standard

The effect of the heat treatments on the tool wear of hybrid Additive Manufacturing of IN718. / Careri, Francesco; Umbrello, Domenico; Essa, Khamis; Attallah, Moataz; Imbrogno, Stano.

In: Wear, Vol. 470-471, 203617, 15.04.2021.

Research output: Contribution to journalArticlepeer-review

Harvard

APA

Vancouver

Author

Bibtex

@article{f8c453f0aa3e426d8ba25dd4532a0fdb,
title = "The effect of the heat treatments on the tool wear of hybrid Additive Manufacturing of IN718",
abstract = "The application of the Direct Energy Deposition (DED) in the aerospace field offers the potential to manufacture and repair critical components. Nevertheless, the parts produced by DED require finishing operations such as machining. Consequently, the tool wear analysis is usually required to better understand the quality of the manufacturing process, especially when difficult-to-machine materials are involved. In this study, the tool wear analysis was carried out after performing machining operations on DED IN718, considering the material as “as-deposited” and “heat-treated” conditions. The microstructural investigation by electron microscopy analysis was performed to study tool wear depending on the variation of the process parameters. The study highlights the presence of different tool wear mechanisms during the machining of the DED IN718. The results demonstrate a correlation between cutting speed, feed rate, material conditions and tool wear. Indeed, although high values of the process parameters (high cutting speed, high feed rate) caused high wear rate, the material conditions affected the tool wear mechanisms involved. It was also found that the main wear mechanisms during the processing of IN718 were adhesive and abrasive. The tools used to machine the heat-treated materials were characterised by extreme wear as suggested by the crater formation, due to the superior mechanical properties exhibited by the material.",
keywords = "Additive manufacturing, Machining, Superalloys, Tool wear, Electron microscopy",
author = "Francesco Careri and Domenico Umbrello and Khamis Essa and Moataz Attallah and Stano Imbrogno",
note = "Funding Information: The authors would like to acknowledge the European research project that funded this research. The project belongs to Horizon 2020 research and innovation programme Novel ALL–IN–ONE machines, robots and systems for affordable, worldwide and lifetime Distributed 3D hybrid manufacturing and repair operations (Project ID: 723795). Publisher Copyright: {\textcopyright} 2021 Elsevier B.V.",
year = "2021",
month = apr,
day = "15",
doi = "10.1016/j.wear.2021.203617",
language = "English",
volume = "470-471",
journal = "Wear",
issn = "0043-1648",
publisher = "Elsevier",

}

RIS

TY - JOUR

T1 - The effect of the heat treatments on the tool wear of hybrid Additive Manufacturing of IN718

AU - Careri, Francesco

AU - Umbrello, Domenico

AU - Essa, Khamis

AU - Attallah, Moataz

AU - Imbrogno, Stano

N1 - Funding Information: The authors would like to acknowledge the European research project that funded this research. The project belongs to Horizon 2020 research and innovation programme Novel ALL–IN–ONE machines, robots and systems for affordable, worldwide and lifetime Distributed 3D hybrid manufacturing and repair operations (Project ID: 723795). Publisher Copyright: © 2021 Elsevier B.V.

PY - 2021/4/15

Y1 - 2021/4/15

N2 - The application of the Direct Energy Deposition (DED) in the aerospace field offers the potential to manufacture and repair critical components. Nevertheless, the parts produced by DED require finishing operations such as machining. Consequently, the tool wear analysis is usually required to better understand the quality of the manufacturing process, especially when difficult-to-machine materials are involved. In this study, the tool wear analysis was carried out after performing machining operations on DED IN718, considering the material as “as-deposited” and “heat-treated” conditions. The microstructural investigation by electron microscopy analysis was performed to study tool wear depending on the variation of the process parameters. The study highlights the presence of different tool wear mechanisms during the machining of the DED IN718. The results demonstrate a correlation between cutting speed, feed rate, material conditions and tool wear. Indeed, although high values of the process parameters (high cutting speed, high feed rate) caused high wear rate, the material conditions affected the tool wear mechanisms involved. It was also found that the main wear mechanisms during the processing of IN718 were adhesive and abrasive. The tools used to machine the heat-treated materials were characterised by extreme wear as suggested by the crater formation, due to the superior mechanical properties exhibited by the material.

AB - The application of the Direct Energy Deposition (DED) in the aerospace field offers the potential to manufacture and repair critical components. Nevertheless, the parts produced by DED require finishing operations such as machining. Consequently, the tool wear analysis is usually required to better understand the quality of the manufacturing process, especially when difficult-to-machine materials are involved. In this study, the tool wear analysis was carried out after performing machining operations on DED IN718, considering the material as “as-deposited” and “heat-treated” conditions. The microstructural investigation by electron microscopy analysis was performed to study tool wear depending on the variation of the process parameters. The study highlights the presence of different tool wear mechanisms during the machining of the DED IN718. The results demonstrate a correlation between cutting speed, feed rate, material conditions and tool wear. Indeed, although high values of the process parameters (high cutting speed, high feed rate) caused high wear rate, the material conditions affected the tool wear mechanisms involved. It was also found that the main wear mechanisms during the processing of IN718 were adhesive and abrasive. The tools used to machine the heat-treated materials were characterised by extreme wear as suggested by the crater formation, due to the superior mechanical properties exhibited by the material.

KW - Additive manufacturing

KW - Machining

KW - Superalloys

KW - Tool wear

KW - Electron microscopy

UR - http://www.scopus.com/inward/record.url?scp=85099636064&partnerID=8YFLogxK

U2 - 10.1016/j.wear.2021.203617

DO - 10.1016/j.wear.2021.203617

M3 - Article

AN - SCOPUS:85099636064

VL - 470-471

JO - Wear

JF - Wear

SN - 0043-1648

M1 - 203617

ER -