Sintering and concomitant crystallization of bioactive glasses

Research output: Contribution to journalArticle

Colleges, School and Institutes

Abstract

The sintering of bioactive glasses allows for the preparation of complex structures, such as three‐dimensional porous scaffolds. Such 3D constructs are particularly interesting for clinical applications of bioactive glasses in bone regeneration, as the scaffolds can act as a guide for bone cells growing in, allowing for good integration with existing and newly formed tissue while the scaffold slowly degrades. Owing to the pronounced tendency of many bioactive glasses to crystallise upon heat treatment, 3D scaffolds have not been much exploited commercially. Here, the influence of crystallisation on the sintering behaviour of several bioactive glasses is investigated. In a series of mixed‐alkali glasses an increased CaO/alkali metal oxide ratio improved sintering compared to Bioglass 45S5, where dense sintering was inhibited. Addition of small amounts of calcium fluoride helped to keep melting and sintering temperatures low. Unlike glass 13‐93, these new glasses crystallised during sintering but this did not prevent densification. Variation in bioactive glass particle size allowed for fine‐tuning the microporosity resulting from the sintering process.

Details

Original languageEnglish
JournalInternational Journal of Applied Glass Science
Early online date21 Jun 2019
Publication statusE-pub ahead of print - 21 Jun 2019

Keywords

  • Bioactive glass, Sintering, Crystallisation, Scaffolds