Effects of low Ag additions on the hydrogen permeability of Pd–Cu–Ag hydrogen separation membranes

Shahrouz Nayebossadri, John Speight, David Book

Research output: Contribution to journalArticlepeer-review

46 Citations (Scopus)
457 Downloads (Pure)

Abstract

Pd–Cu alloys are of potential interest for use as hydrogen purification membranes, but have relatively low permeability compared to the commercially used alloys such as Pd–Ag. In this work, the effects of partial Ag substitution on the hydrogen diffusivity, solubility and the permeability of Pd–Cu membranes with a bcc structure have been investigated. With the addition of 2.3 and 3.9 at% Ag to Pd–Cu, lattice expansions of 0.11% and 0.35% were observed. Structural analyses by in-situ XRD showed that the bcc structure of the 2.3 at% Ag alloy is retained upon heating to 600 °C, whereas an fcc phase forms in the 3.9 at% Ag alloy resulting in a mixed (bcc+fcc) structure. Whilst the diffusion coefficients between 350 and 400 °C for both Pd–Cu–Ag ternary samples were shown to be lower than their binary alloys (which had similar structures), higher solubility values were obtained. The lower diffusion coefficients of the ternary alloys are related to an increase in the diffusion activation barrier in the presence of Ag, and the higher solubility values may be attributed to the lattice expansion and high Ag–H chemical interaction. Hydrogen permeation measurements showed that an enhancement in the hydrogen solubility of the bcc phase Pd45.8Cu51.9Ag2.3, does not have a substantial effect on the permeability of the membrane. In contrast, for the Pd45.1Cu51Ag3.9 sample with a mixed (bcc+fcc) phase, higher hydrogen solubility can lead to a remarkable improvement in permeability. Hence, it is suggested that the hydrogen permeability in the bcc phase is mainly controlled by hydrogen diffusion, and the solubility enhancement can only significantly improve the hydrogen permeability when the fcc phase is present.

Original languageEnglish
Pages (from-to)216-225
JournalJournal of Membrane Science
Volume451
Early online date8 Oct 2013
DOIs
Publication statusPublished - 1 Feb 2014

Keywords

  • Hydrogen separation
  • Metallic membrane
  • Palladium-based ternary alloys
  • Pd–Cu
  • Pd–Cu–Ag

Fingerprint

Dive into the research topics of 'Effects of low Ag additions on the hydrogen permeability of Pd–Cu–Ag hydrogen separation membranes'. Together they form a unique fingerprint.

Cite this