Damage in extrusion additive manufactured biomedical polymer: Effects of testing direction and environment during cyclic loading

Amirpasha Moetazedian, Andrew Gleadall*, Elisa Mele, Vadim V. Silberschmidt

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

42 Downloads (Pure)

Abstract

Although biodegradable polymers were widely researched, this is the first study considering the effect of combined testing environments and cyclic loading on the most important aspect related to additive manufacturing: the interfacial bond between deposited layers. Its results give confidence in applicability of the material extrusion additive manufacturing technology for biomedical fields, by demonstrating that the interface behaves in a manner similar to that of the bulk-polymer material. To do this, especially designed tensile specimens were used to analyse the degradation of 3D-printed polymers subjected to constant-amplitude and incremental cyclic loads when tested in air at room temperature (control) and submerged at 37 °C (close to in-vivo conditions). The mechanical properties of the interface between extruded filaments were compared against the bulk material, i.e. along filaments. In both cases, cyclic loading caused only a negligible detrimental effect compared to non-cyclic loading (less than 10 % difference in ultimate tensile strength), demonstrating the suitability of using 3D-printed components in biomedical applications, usually exposed to cyclic loading. For cyclic tests with a constant loading amplitude, larger residual deformation (>100 % greater) and energy dissipation (>15 % greater) were found when testing submerged in solution at 37 °C as opposed to in laboratory conditions (air at room temperature), as used by many studies. This difference may be due to plasticisation effects of water and temperature. For cyclic tests with incrementally increasing loading amplitudes, the vast majority of energy dissipation happened in the last two cycles prior to failure, when the polymer approached the yield point. The results demonstrate the importance of using an appropriate methodology for biomedical applications; otherwise, mechanical properties may be overestimated.

Original languageEnglish
Article number104397
Number of pages11
JournalJournal of the Mechanical Behavior of Biomedical Materials
Volume118
Early online date20 Feb 2021
DOIs
Publication statusPublished - Jun 2021

Bibliographical note

Copyright © 2021 Elsevier Ltd. All rights reserved.

Keywords

  • Additive manufacturing
  • Damage
  • Interface
  • Polylactide
  • Submerged

ASJC Scopus subject areas

  • Biomaterials
  • Biomedical Engineering
  • Mechanics of Materials

Fingerprint

Dive into the research topics of 'Damage in extrusion additive manufactured biomedical polymer: Effects of testing direction and environment during cyclic loading'. Together they form a unique fingerprint.

Cite this