Cutting temperatures when ball nose end milling γ-TiAl intermetallic alloys

Research output: Contribution to journalArticlepeer-review

Abstract

Experimental results are presented for Ti–45Al–2Mn–2Nb + 0.8 vol% TiB2XD and Ti–45Al–8Nb–0.2C alloys. Three approaches were employed involving a constantan-workpiece thermocouple arrangement, implanted K-type thermocouples and IR thermography. New and worn (~300 μm flank wear) coated carbide tools were used under dry conditions when down milling at 50–345 m/min, with workpieces mounted horizontally and at 45°. Despite slight variation in ancillary finishing parameters there was generally good agreement between data sets for the different evaluation techniques employed and for both alloys. Higher temperatures were measured with the workpiece at 45°, with constantan-workpiece thermocouple temperatures of 375 °C and 413 °C for new and worn tools respectively at 345 m/min.

Details

Original languageEnglish
Pages (from-to)75-78
Number of pages4
JournalCIRP Annals - Manufacturing Technology
Volume62
Issue number1
Early online date10 Apr 2013
Publication statusPublished - 2013

Keywords

  • Temperature, Titanium, Milling