Abstract
One major problem with ball and socket artificial discs is the migration of wear particles to the surrounding tissues. This debris can cause inflammation that can lead to implant loosening. Encapsulating the artificial disc with an elastomer sheath, could prevent this problem by retaining the wear particles within the disc. The encapsulation sheath will face millions of tensile cycles during the implant life and, therefore, it must have the ability to withstand large strains without fracture. Using cyclic displacement, crack nucleation was applied on dumbbell specimens and crack growth was applied on rectangular specimens with an initial crack. Both tests were performed on Silex silicone and polyurethane ether
elastomer specimens, both with a Shore durometer hardness of 40 shore A. No samples completely failed during the crack nucleation tests after five million cycles. The polyurethane ether elastomer showed a slower rate of crack growth life (421k cycles to reach 70 mm crack length) than silicone elastomer (221k cycles to reach the same crack length) in the control group. Accelerated ageing decreased the hardness and the crack growth rate of the polyurethane elastomer but had the opposite effect for the silicone elastomer. Gamma sterilization increased the crack growth rate and did not affect the hardness of the polyurethane elastomer. The hardness and the crack growth rate of the
silicone elastomer were increased after gamma sterilization.
elastomer specimens, both with a Shore durometer hardness of 40 shore A. No samples completely failed during the crack nucleation tests after five million cycles. The polyurethane ether elastomer showed a slower rate of crack growth life (421k cycles to reach 70 mm crack length) than silicone elastomer (221k cycles to reach the same crack length) in the control group. Accelerated ageing decreased the hardness and the crack growth rate of the polyurethane elastomer but had the opposite effect for the silicone elastomer. Gamma sterilization increased the crack growth rate and did not affect the hardness of the polyurethane elastomer. The hardness and the crack growth rate of the
silicone elastomer were increased after gamma sterilization.
Original language | English |
---|---|
Pages (from-to) | 225-234 |
Journal | Polymer Testing |
Volume | 62 |
Early online date | 5 Jul 2017 |
DOIs | |
Publication status | Published - 1 Sept 2017 |
Keywords
- Accelerated ageing
- Crack growth
- Crack nucleation
- Gamma sterilization
- Polyurethane ether and Silicone elastomers