Structural characteristics of low temperature plasma carburised austenitic stainless steel

Y. Sun*, X. Li, T. Bell

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

98 Citations (Scopus)

Abstract

A low temperature plasma carburising process has recently been developed to engineer the surfaces of austenitic stainless steels to achieve combined improvements in wear and corrosion resistance. The present paper discusses the structural characteristics of the carburised layers produced on AISI type 316 steel at temperatures between 400 and 600°C. It was found that at low temperatures (<520°C), the carburised layers produced were precipitation free and comprised a single phase, which had a face centred cubic structure and was identified as expanded austenite owing to the supersaturation of carbon in austenite. The carburised layer was in a deformed and distorted state. High densities of twins, stacking faults, and dislocations were found in the expanded austenite. The degree of lattice expansion was estimated and was found to vary with processing temperature and depth in the layer. Precipitation of carbides (mainly Cr7C3) occurred when the carburising temperature was relatively high (for example 550 and 600°C). In addition, stress induced martensite was found, particularly in the carburised layers produced at relatively high temperatures.

Original languageEnglish
Pages (from-to)1171-1178
Number of pages8
JournalMaterials Science and Technology
Volume15
Issue number10
DOIs
Publication statusPublished - Oct 1999

ASJC Scopus subject areas

  • General Materials Science
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint

Dive into the research topics of 'Structural characteristics of low temperature plasma carburised austenitic stainless steel'. Together they form a unique fingerprint.

Cite this