Influence of forging pressure on microstructural and mechanical properties development in linear friction welded al-cu dissimilar joint

Nan Zhou, Chunlei Gan, Dongfu Song, Wenjun Qi, Moataz M. Attallah

Research output: Contribution to journalArticlepeer-review

Abstract

Dissimilar AA5083 and C101 pure copper linear friction welds were prepared using different forging pressures (60 MPa, 80 MPa, and 110 MPa) to investigate the influence of the forging pressure on the microstructural and mechanical properties development using optical microscopy (OM), scanning electron microscopy (SEM), hardness measurements, and tensile testing. The in-situ generated intermetallic particles in the vicinity of the weld line were characterised using electron probe micro-analyser (EPMA), to rationalise their impact on the mechanical properties. The results showed that the process led to the formation of various intermetallic phases as well as the entrainment of base material fragments in the vicinity of the weld interface. In general, high forging pressure corresponding to high welding heat input resulted in the formation of a layered intermetallic phase (identified as Al2CuMg), which was the most detrimental to the mechanical properties, compared with a scattered distribution of fragmented Cu and intermetallic particles across the joint interface.

Original languageEnglish
Article numbere2401
JournalSoldagem e Inspecao
Volume24
DOIs
Publication statusPublished - 1 Jan 2019

Keywords

  • Forging pressure
  • Intermetallic compound
  • Linear friction welding (LFW)
  • Mechanical properties

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys

Fingerprint

Dive into the research topics of 'Influence of forging pressure on microstructural and mechanical properties development in linear friction welded al-cu dissimilar joint'. Together they form a unique fingerprint.

Cite this